Method for manufacturing semiconductor device having thinned fins

ABSTRACT

Provided is a stable manufacturing method for a semiconductor device. In the manufacturing method for a semiconductor device, first, fins with an equal width are formed in each of a memory cell portion and a logic portion of a semiconductor substrate. Then, the fins in the logic portion are etched with the fins in the memory cell covered with a mask film, thereby fabricating fins in the logic portion, each of which is narrower than the fin formed in the memory cell portion.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a Divisional of U.S. patent application Ser. No.15/409,947, filed on Jan. 19, 2017, which claims the benefit of JapanesePatent Application No. 2016-033597 filed on Feb. 24, 2016 including thespecification, drawings, and abstract is incorporated herein byreference in its entirety.

BACKGROUND

The present invention relates to a method for manufacturing asemiconductor device, and more particularly, to a technique suitable foruse in a method for manufacturing a semiconductor device, for example, anon-volatile memory.

An Electrically Erasable and Programmable Read-Only Memory (EEPROM) iswidely used as a non-volatile semiconductor storage device that can beelectrically written and erased. Such a storage device, typified by aflash memory widely used at present, includes a conductive floating gateelectrode or trap insulating film enclosed by an oxide film and locatedunder a gate electrode of a Metal-Insulator-Semiconductor Field-EffectTransistor (MISFET) The storage device stores a charge stored state inthe floating gate or trap insulating film as storage information, whichcan be read therefrom as a threshold for a transistor. The trapinsulating film is an insulating film capable of storing chargestherein, and is made of a silicon nitride film by way of example. Theinjection and release of charges into such a charge storage regionshifts the threshold of the MISFET, causing the storage device, such asthe flash memory, to act as a storage element. This type of flash memoryis, for example, a split gate cell using aMetal-Oxide-Nitride-Oxide-Semiconductor (MONOS) film. Such a memory usesthe silicon nitride film in the charge storage region to discretelystore charges therein, compared to when using a conductive floating gatefilm, thereby achieving excellent reliability of data retention.Furthermore, this memory has the excellent reliability of dataretention, and thus has various advantages that oxide films positionedabove and below the silicon nitride film can be thinned, enablingwriting and erasing operations at lower voltages.

The memory cell includes: a control gate electrode (select gateelectrode) formed over a semiconductor substrate via a first gateinsulating film; a memory gate electrode formed over the semiconductorsubstrate via a second gate insulating film containing the chargestorage region; and a pair of semiconductor regions (source region anddrain region) formed at the surface of the semiconductor substrate tosandwich therebetween the control gate electrode and the memory gateelectrode.

Japanese Unexamined Patent Application Publication No. 2006-41354(Patent Document 1) discloses a memory cell in which a control gateelectrode and a memory gate electrode are arranged to stride across aconvex active region formed at the surface of the semiconductorsubstrate.

Japanese Unexamined Patent Application Publication No. 2013-98192(Patent Document 2) discloses a technique that uses isotropic etching toshorten the length of a sidewall as described in paragraphs [0128] to[0135] with reference to FIGS. 39 to 41.

Patent Document 1: Japanese Unexamined Patent Application PublicationNo. 2006-41354

Patent Document 2: Japanese Unexamined Patent Application PublicationNo. 2013-98192

SUMMARY

Patent Document 1 describes an invention that relates to a fin-typenon-volatile memory. A sixth embodiment discloses an example in whichthe memory gate electrode only in the memory cell has a convex shape(fin shape), and the control gate electrode and a logic portion areformed as normal flat devices.

However, to reduce the areas and power consumption of not only a memorycell portion, but also a logic portion, MISFETs in both the memory cellportion and the logic portion need to be or a fin-type.

It is desired to develop a stable process for forming a semiconductordevice with a non-volatile memory that includes fin-type MISFETs in amemory cell portion and a logic portion.

Other problems and new features of the present invention will be clearlyunderstood by the following detailed description with reference to theaccompanying drawings.

According to one embodiment, a method for manufacturing a semiconductordevice is provided which includes the steps of: providing asemiconductor substrate with a main surface; forming a first mask filmin each of a first region and a second region of the main surface of thesemiconductor substrate; and forming a second mask film over sidewallsof the first mask film in each of the first region and the secondregion. The method further includes the steps of: after removing thefirst mask film, forming a first convex portion under the second maskfilm by providing concave portions through etching of parts of thesemiconductor substrate located outside the second mask films in thefirst and second regions, the first convex portion having a first width;and forming a second convex portion in the second region by etching thefirst convex portion in the second region while covering the firstconvex portion in the first region with a third mask film, the secondconvex portion in the second region having a second width. The secondwidth is narrower than the first width.

Accordingly, the one embodiment of the present invention can provide astable manufacturing method for a semiconductor device.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a cross-sectional view of a main part of a manufacturing stepin a manufacturing method for a semiconductor device in a consideredexample;

FIG. 2 is a cross-sectional view of a main part in another manufacturingstep for the semiconductor device, following the step shown in FIG. 1;

FIG. 3 is a cross-sectional view of a main part in another manufacturingstep for the semiconductor device, following the step shown in FIG. 2;

FIG. 4 is a cross-sectional view of a main part in another manufacturingstep for the semiconductor device, following the step shown in FIG. 3;

FIG. 5 is a cross-sectional view of a main part in another manufacturingstep for the semiconductor device, following the step shown in FIG. 4;

FIG. 6 is a cross-sectional view of a main part in another manufacturingstep for the semiconductor device, following the step shown in FIG. 5;

FIG. 7 is a cross-sectional view of a main part in another manufacturingstep for the semiconductor device, following the step shown in FIG. 6;

FIG. 8 is a cross-sectional view of a main part in another manufacturingstep for the semiconductor device, following the step shown in FIG. 7;

FIG. 9 is a cross-sectional view of a main part in another manufacturingstep for the semiconductor device, following the step shown in FIG. 8;

FIG. 10 is a plan view of a main part of the semiconductor device in oneembodiment;

FIG. 11 is a cross-sectional view of the main part of the semiconductordevice in the one embodiment;

FIG. 12 is a cross-sectional view of a main part of the semiconductordevice in the one embodiment;

FIG. 13 is a cross-sectional view of a main part in a manufacturing stepfor the semiconductor device in the one embodiment;

FIG. 14 is a cross-sectional view of a main part in anothermanufacturing step for the semiconductor device, following the stepshown in FIG. 13;

FIG. 15 is a cross-sectional view of a main part in anothermanufacturing step for the semiconductor device, following the stepshown in FIG. 14;

FIG. 16 is a cross sectional view of a main part of the semiconductordevice in FIG. 15;

FIG. 17 is a cross-sectional view of a main part in anothermanufacturing step for the semiconductor device, following the stepshown in FIG. 16;

FIG. 18 is across-sectional view of a main part in another manufacturingstep for the semiconductor device, following the step shown in FIG. 17;

FIG. 19 is a cross-sectional view of a main part in anothermanufacturing step for the semiconductor device, following the stepshown in FIG. 18;

FIG. 20 is a cross-sectional view of a main part in anothermanufacturing step for the semiconductor device, following the stepshown in FIG. 19;

FIG. 21 is a cross-sectional view of a main part in anothermanufacturing step for the semiconductor device, following the stepshown in FIG. 20;

FIG. 22 is a cross-sectional view of a main part in anothermanufacturing step for the semiconductor device, following the stepshown in FIG. 21;

FIG. 23 is a cross-sectional view of a main part in anothermanufacturing step for the semiconductor device, following the stepshown in FIG. 22;

FIG. 24 is a cross-sectional view of a main part in anothermanufacturing step for the semiconductor device, following the stepshown in FIG. 23;

FIG. 25 is a cross-sectional view of a main part in anothermanufacturing step for the semiconductor device, following the stepshown in FIG. 24;

FIG. 26 is a cross-sectional view of a main part of the semiconductordevice in the same step as that in FIG. 25 (but at a different positionfrom that shown in FIG. 25);

FIG. 27 is a cross-sectional view of a main part in anothermanufacturing step for the semiconductor device, following the stepshown in FIG. 25;

FIG. 28 is a cross-sectional view of a main part in anothermanufacturing step for the semiconductor device, following the stepshown in FIG. 27;

FIG. 29 is a cross-sectional view of a main part or a manufacturing stepin a manufacturing method for a semiconductor device in a modifiedexample;

FIG. 30 is a cross-sectional view of a main part in anothermanufacturing step for the semiconductor device, following the stepshown in FIG. 29; and

FIG. 31 is a cross-sectional view of a main part in anothermanufacturing step for the semiconductor device, following the stepshown in FIG. 30.

DETAILED DESCRIPTION

The following preferred embodiments of the invention may be describedbelow by being divided into a plurality of sections or embodiments forconvenience, if necessary, which are not independent from each otherunless otherwise specified. One of the sections or embodiments may be amodified example, a detailed description, supplementary explanation, andthe like of a part or all of the other. Even when referring to aspecific number regarding an element and the like (including the numberof elements, a numerical value, an amount, a range, and the like) in theembodiments below, the invention is not limited to the specific number.The invention may take the number greater than, or less than thespecific number, unless otherwise specified, and except when obviouslylimited to the specific number in principle. The components (includingsteps) in the embodiments below are not necessarily essential unlessotherwise specified and except when clearly considered to be essentialin principle. Likewise, when referring to the shape of one component orthe positional relationship between the components in the followingembodiments and the like, any shape or positional relationshipsubstantially similar or approximate to that described herein may beincluded in the invention unless otherwise specified and except whenclearly considered not to be so in principle. The same goes for theabove numerical value and the range.

Some embodiments of the present invention will be described in detailbelow based on the accompanying drawings. In all drawings for explainingthe embodiments, parts having the same function are indicated by thesame or similar reference characters, and the repeated descriptionthereof will be omitted. In the embodiments below, the description ofthe same or similar parts will not be repeated in principle, except whenneeded.

In the accompanying drawings used in the embodiments, even somecross-sectional views may omit hatching for easy understanding.Furthermore, some plan views are provided with hatching to make themmore easily understood.

EMBODIMENTS Considered Example

The inventors have studied and considered semiconductor devices with aplurality of fin-type MISFETs arranged in a memory cell portion with anon-volatile memory and a logic portion. First, a description will begiven on a formation method for a fin-type element formation region(active region), which is part of a formation method for a semiconductordevice. The fin-type element formation region (active region) will besimply called a “fin” or a “convex portion”. As will be described later,a semiconductor device having a non-volatile memory considered by theinventors of the present application is required to have a structureincluding a memory cell portion with a wide fin width and a logicportion with a narrow fin width. That is, the fin width of the logicportion needs to be narrower than that of the memory cell portion. FIGS.1 to 9 are cross-sectional views of main parts of formation steps in amanufacturing method for a semiconductor device in a considered example,particularly showing a fin formation step.

As shown in FIG. 1, a provision step for a semiconductor substrate (stepS1) and an insulating-film formation step (step S2) are performed. Inthe provision step for the semiconductor substrate (step S1), asemiconductor substrate 1 made of p-type monocrystalline silicon andhaving, for example, a specific resistance of approximately 1 to 10 Ωcmis provided. The semiconductor substrate 1 is a semiconductor waferhaving a diameter of 200 mm to 300 mm. The main surface of thesemiconductor substrate 1 has a memory cell portion A and a logicportion B. A plurality of MISFETs is formed in each of the memory cellportion A and the logic portion B. The insulating-film formation step(step S2) includes a step of forming an insulating film 2 over a surfaceof the semiconductor substrate 1, and a step of forming an insulatingfilm 3 over the insulating film 2. The insulating film 2 is made of asilicon oxide film with a thickness of approximately 2 to 10 nm, and theinsulating film 3 is made of a silicon nitride film with a thickness ofapproximately 20 to 100 nm. Furthermore, as shown in FIG. 1, a mask film4 is formed over the insulating film 3 to carry out a deposition step ofthe mask film 4. The mask film 4 is, for example, made of an amorphoussilicon film having a thickness of 20 to 200 nm.

Then, as shown in FIG. 2, a patterning step of the mask film 4 iscarried out. The mask film 4 is patterned by using the photolithographyand etching techniques, thereby forming a plurality of mask films 4 a inthe memory cell portion A as well as a plurality of mask films 4 b inthe logic portion B. The deposition step of the mask film 4 shown inFIG. 1 and the patterning step of the mask film 4 are collectivelyreferred to as a mask-film formation step (step S3). The formationpositions of fins (spacing between adjacent fins) can be determined bythe widths of the mask film 4 a and 4 b, a spacing between the maskfilms 4 a, and a spacing between the mask films 4 b. The width of themask film 4 b and the spacing between the adjacent mask films 4 b areset narrower, compared to the mask film 4 a.

Then, as shown in FIG. 3, a formation step of the insulating film 5 iscarried out. The insulating film 5 is deposited over the main surface ofthe semiconductor substrate 1 to cover the upper surfaces and sidesurfaces of the mask films 4 a and 4 b. The insulating film 5 is madeof, for example, a silicon oxide film having a thickness of 10 to 40 nm.The thickness of the insulating film 5 can determine the width of thefin.

Then, as shown in FIG. 4, in a formation step of hard mask films 5 a and5 b, the above-mentioned insulating film 5 is subjected to anisotropicdry etching, whereby the hard mask films 5 a and 5 b are selectivelyformed of sidewall insulating films over the sidewalls of the mask films4 a and 4 b. The hard mask film 5 a is formed in the memory cell portionA, while the hard mask film 5 b is formed in the logic portion B. Thehard mask films 5 a and 5 b are equal in width. Furthermore, each of thehard mask films 5 a and 5 b has substantially the same thickness as theinsulating film 5 described above. After forming the hard mask films 5 aand 5 b, the mask films 4 a and 4 b are removed.

Then, as shown in FIG. 5, a line-thinning step of the hard mask film 5 bis carried out. A photoresist film (mask film) PR1 is formed to coverthe memory cell portion A while exposing the logic portion B. Isotropicetching is applied to the hard mask films 5 b in the logic portion Bexposed from the photoresist film PR1. When the hard mask film is formedof a silicon oxide film, the isotropic dry etching is difficult toperform from the technical perspective, and thus wet etching isgenerally applied. In this way, hard mask films 5 b′, each having anarrower width than the above-mentioned hard mask film 5 a, are formedin the logic portion B. That is, the line-thinning step is a step ofdecreasing (reducing) a width of the hard mask film 5 b described above.After forming the hard mask films 5 b′, the resist film PR1 is removed.In this way, the hard mask films 5 a and 5 b′ for formation of fins areformed in the memory cell portion A and the logic portion B,respectively. Here, the formation step of the insulating film 5, theformation step of the hard mask films 5 a and 5 b, and the line-thinningstep of the hard mask film 5 b are collectively called a “hard-mask-filmformation step (step S4)”.

Then, as shown in FIG. 6, a fin processing step (step S5) is carriedout. Anisotropic dry etching is applied to the insulating films 3 and 2and the semiconductor substrate 1 using the hard mask films 5 a and 5 b′as a mask, thereby producing the insulating films 3 and 2 withsubstantially the same shape in the planar view as the hard mask films 5a and 5 b′, as well as the fins F1 and F2. That is, concave portions areformed in the semiconductor substrate 1 outside each of the hard maskfilms 5 a and 5 b′ (i.e., in regions not covered with the hard maskfilms 5 a and 5 b′), thereby forming the fins F1 and F2, which areconvex portions enclosed by the concave portions. Here, when etching thesemiconductor substrate 1, the insulating film 3 is also used as anetching mask. In this way, parts of the semiconductor substrate 1located in regions exposed from the hard mask films 5 a and 5 b′ arelowered by 100 to 250 nm, resulting in formation of the fins F1 and F2,each having a height of 100 to 250 am from a main surface 1 a of thesemiconductor substrate 1. It is apparent that a width W1 of the fin F1in the memory cell portion A is wider than a width W2 of the fin F2 inthe logic portion B.

Then, as shown in FIG. 7, a deposition step of an insulating film 6 iscarried out. The insulating film 6 made of a silicon oxide film or thelike is deposited over the semiconductor substrate 1 to completely fillthe fins F1 and F2, the insulating films 2 and 3, and the hard maskfilms 5 a and 5 b′. That is, the insulating film 6 is formed in theconcave portions around each convex portion.

Then, as shown in FIG. 8, a polishing step of the insulating film 6 iscarried out. A Chemical Mechanical Polishing (CMP) process is performedon the insulating film 6, the hard mask films 5 a and 5 b′ describedabove, and the insulating film 3. After polishing the hard mask films 5a and 5 b′, the insulating films 3 and 6 are polished until thethickness of the insulating film 3 reaches, for example, approximately20 nm.

Then, as shown in FIG. 9, an etch-back step of the insulating film 6 iscarried out. After completion of the above-mentioned polishing step,first, the insulating film 3 is removed, for example, by wet etching.Then, the isotropic etching is applied to the insulating film 6 tothereby form element isolation films 6 a and 6 b. That is, the uppersurface of the insulating film 6 is lowered to set the height of each ofthe fins F1 and F2, for example, at approximately 30 nm to 50 nm. Here,the deposition step of the insulating film 6, the polishing step of theinsulating film 6, and the etch-back step of the insulating film 6 arecollectively called a fin formation step (step S6). Note that in theisotropic etching step of the insulating film 6, the insulating film 2is also removed.

Throughout the steps described above, the fins F1 can be formed in thememory cell portion A, while the fins F2 can be formed in the logicportion B. Each of the fins F1 and F2 is a convex portion that protrudesfrom the main surface 1 a of the semiconductor substrate 1. The fins F1and F2 are enclosed by the element isolation films 6 a and 6 b,respectively, formed over the main surface 1 a of the semiconductorsubstrate 1. That is, the adjacent fins F1 are separated from each otherby the element isolation film 6 a, while the adjacent fins F2 areseparated from each other by the element isolation film 6 b. The fin F1includes a non-volatile memory cell, while the fin F2 includes a MISFET,as will be described later.

Studies by the inventors show that there is some room for furtherimprovement in the above-mentioned fin formation method.

First, in the line-thinning step of the hard mask film 5 b in theabove-mentioned hard-mask-film formation step (step S4), suppose thatthe hard mask film 5 b is wet-etched with hydrofluoric acid. In such acase, the etching amount is difficult to control, resulting in largevariations in the etching amount, and in the size (width, length, orheight) of the hard mask film 5 b′ on the plane of a semiconductorwafer. Variations in the etching amount and in the size of the hard maskfilm 5 b′ directly lead to variations in the width of the fin, whichcauses variations in the characteristics of the MISFETs formed thereat.

Secondly, in the formation process of the insulating film 5 in theabove-mentioned hard-mask-film formation step (step S4), the thicknessof the insulating film 5 is set to the width of the hard mask film 5 ain the memory cell portion A, which is larger than the width of the hardmask film 5 b′ in the logic portion B. For this reason, in a stage wherethe insulating film 5 is deposited, an interval between the adjacentmask films 4 b in the logic portion B is filled with the insulating film5. Even the anisotropic dry etching on the insulating film 5 in theformation step of the hard mask films 5 a and 5 b fails to form the hardmask film 5 b, which appears to be a problem. In particular, theminiaturization of the MISFET formed in the logic portion B is found tomake this type of problem worse.

<Device Structure of Semiconductor Device>

FIG. 10 shows a plan view of a main part of the semiconductor device inthis embodiment. Referring to FIG. 10, the memory cell portion Acorresponds to a plan view of a main part of a memory cell array havinga plurality of memory cells arranged in rows and columns, while thelogic portion B corresponds to a plan view of a main part of atransistor Tr that configures a logic circuit and the like in a logiccircuit formation region. While an n-type Metal Insulator SemiconductorField Effect Transistor (MISFET) is exemplified as the transistor Tr, ap-type MISFET can also be formed in the same way. FIG. 11 shows across-sectional view of a main part of the memory cell portion in thesemiconductor device in this embodiment. FIG. 11 illustrates fourcross-sectional views of the memory cell portion A, in which a memorycell portion A1 corresponds to a cross-sectional view taken along theline A1-A1′ of FIG. 10; a memory cell portion A2 to a cross-sectionalview along the line A2-A2′ of FIG. 10; a memory cell portion A3 to across-sectional view along the line A3-A3′ of FIG. 10; and a memory cellportion A4 to a cross-sectional view along the line A4-A4′ of FIG. 10.FIG. 12 shows three cross-sectional views of the logic portion B. Alogic portion B1 corresponds to a cross-sectional view taken along theline B1-B1′ of FIG. 10; a logic portion B2 to a cross-sectional viewalong the line B2-B2′ of FIG. 10; and a logic portion B3 to across-sectional view along the line B3-B3′ of FIG. 10.

As shown in FIG. 10, in the memory cell portion A, fins FA extending inthe X direction are arranged at equal intervals in the Y direction. Eachof the fins FA is, for example, a protrusion (convex portion) in arectangular parallelepiped shape that selectively protrudes from themain surface 1 a of the semiconductor substrate 1. Each fin FA has itslower end part enclosed by an element isolation film STM that covers themain surface 1 a of the semiconductor substrate 1. The fins FA are partsof the semiconductor substrate 1 and serve as the active regions of thesemiconductor substrate 1. Thus, in the planar view, a region betweenthe adjacent fins FA is filled with the element isolation film STM, andeach fin FA is enclosed by the element isolation film STM. The fins FAserve as the active regions for forming the memory cells MC.

On the fins FA, a plurality of control gate electrodes CG and aplurality of memory gate electrodes MG are arranged to extend in the Ydirection (i.e., in the direction perpendicular to the X direction). Adrain region MD is formed on the side of the control gate electrode CG,and a source region MS is formed on the side of the memory gateelectrode MG in such a manner as to sandwich the control gate electrodeCG and the memory gate electrode MG between these regions. The drainregion MD and the source region MS are semiconductor regions with n-typeimpurities introduced into the fin FA. Epilayers EP2 and EP1 are formedaround the fins FA. That is, the drain region MD is an n-typesemiconductor region in which n-type impurities are introduced into thefin FA and the epilayer EP2. The source region MS is an n-typesemiconductor region in which n-type impurities are introduced into thefin FA and the epilayer EP1. The drain region MD is formed between theadjacent two control gate electrodes CG, while the source region MS isformed between the adjacent two memory gate electrodes MG. The memorycell MC includes the control gate electrode CG, the memory gateelectrode MG, the drain region MD, and the source region MS.

Either the drain region MD or the source region MS is shared between thetwo memory cells MC adjacent in the X direction. The two memory cells MCsharing the drain region MD are arranged mirror-symmetrically in the Xdirection with respect to the drain region MD, while the two memorycells MC sharing the source region MS are arranged mirror-symmetricallyin the X direction with respect to the source region MS.

In each fin FA, three or more, or numerous memory cells MC are formed inthe X direction. The drain regions MD of the plurality of memory cellsMC arranged in the X direction are coupled to a source line SL made of ametal wiring MW extending in the X direction via plug electrodes PGformed in contact holes CT. The source regions MS of the plurality ofmemory cells MC arranged in the Y direction are coupled to a bit line BLmade of a metal wire MW extending in the Y direction. The source line SLis preferably formed using the metal wiring located in a different layerfrom that of the bit line BL. For example, the source line SL ispreferably configured of the metal wiring located in an upper layerrelative to the bit line BL.

In the logic portion B, for example, the fins FB are formed to extend inthe X direction. Each of the fins FB is an active region of thesemiconductor substrate 1, like the fin FA. The lower end of the fin FBis enclosed by an element isolation film STL covering the main surface 1a of the semiconductor substrate 1. A gate electrode GE extending in theY direction is disposed over the fin FB. The fin FB has a drain regionLD and a source region LS formed to sandwich the gate electrode GEtherebetween. The drain region LD and the source region LS aresemiconductor regions with n-type impurities introduced into the fin FB.An epilayer EP3 is formed around each fin FB. That is, the drain regionLD and the source region LS are n-type semiconductor regions in whichn-type impurities are introduced into the fin FB and the epilayer EP3.The transistor Tr includes the gate electrode GE, the drain region LD,and the source region LS. The gate electrode GE, the drain region LD,and the source region LS are coupled to the metal wiring MW via the plugelectrodes PG formed in the contact holes CT. The fins FB serve as theactive regions for forming the transistor Tr.

The fins FA and FB are protrusions, for example, having a rectangularparallelepiped shape, which protrude from the main surface 1 a of thesemiconductor substrate 1 in the direction perpendicular to the mainsurface 1 a. The fins FA and FB have any length in the long-sidedirection, any width in the short-side direction, and any height in theheight direction. The fins FA and FB do not necessarily have arectangular parallelepiped shape, and may have a rectangular sectionalshape in the short-side direction with its rounded corner (or corners).In the planer view, the direction in which the fins FA and FB areextended is the long-side direction, and the direction perpendicular tothe long-side direction is a short-side direction. That is, the lengthof the fin is larger than the width thereof. Note that the fins FA andFB are not limited to specific shapes as long as they are protrusionswith a length, a width, and a height. An example of the shape of thefins FA and FB can include a meandering pattern in the planar view.

Next, the structures of the memory cell MC and the transistor Tr will bedescribed with reference to FIGS. 11 and 12.

As shown in FIG. 11, the fins FA as the protrusions of the semiconductorsubstrate 1 are formed in the memory cell portion A of the semiconductorsubstrate 1. Each fin FA has its lower part enclosed by an elementisolation film STM formed over the main surface 1 a of the semiconductorsubstrate 1. That is, the adjacent fins FA are separated from each otherby the element isolation film STM. A p-type well PW1, which is a p-typesemiconductor region, is formed in a lower part of the fin FA. In otherwords, the fin FA is formed within the p-type well PW1.

The control gate electrode CG is formed over a main surface FAa and sidesurfaces FAs of the fin FA via a gate insulating film GIt. The memorygate electrode MG is formed in a region adjacent to the control gateelectrode CG in the long-side direction of the fin FA via a gateinsulating film GIm. The gate insulating film GIm is interposed betweenthe control gate electrode CG and the memory gate electrode MG, so thatthe control gate electrode CG is electrically isolated from the memorygate electrode MG by the gate insulating film GIm. Alternatively, aninsulating film other than the gate insulating film GIm may beinterposed between the control gate electrode CG and the memory gateelectrode MG to electrically isolate these electrodes from each other.

Here, the gate insulating film GIt is a thermally oxidized film (siliconoxide film) formed by thermally oxidizing the main surface FAa and sidesurfaces FAs of the fin FA, which is the protrusion (convex portion) ofthe semiconductor substrate 1 made of silicon. The thickness of the gateinsulating film GIt is 2 nm. The gate insulating film GIm is made of aninsulating film 10′ and an insulating film 11′ formed on the insulatingfilm 10′. The insulating film 10′ is a thermally oxidized film (siliconoxide film) of 5 to 6 nm in thickness that is formed by thermallyoxidizing the main surface FAa and side surfaces FAs of the fin FA,which is the protrusion of the semiconductor substrate 1 made ofsilicon. The insulating film 11′ is configured of a laminated film thatincludes a silicon nitride film serving as a charge storage portion(charge storage layer) and a silicon oxynitride film covering thesurface of the silicon nitride film. The silicon nitride film has athickness of 7 nm, and the silicon oxynitride film has a thickness of 9nm. That is, the gate insulating film GIm has a laminated structure thatincludes a silicon oxide film, a silicon nitride film, and a siliconoxynitride film, the total thickness of the laminated structure being ina range of 21 to 22 nm. Thus, the gate insulating film GIm is thickerthan the gate insulating film GIt under the control gate electrode CG.Alternatively, the gate insulating film GIm may have a laminatedstructure that includes a silicon oxide film, a silicon nitride film,and a silicon oxide film which are stacked in this order.

In the memory cell portion A2, in the short-side direction of the finFA, the control gate electrode CG extends along the main surface FAa andside surfaces FAs of the fin FA via the gate insulating film GIt, andalso extends over the element isolation film STM that encloses the finFA. That is, the control gate electrode CG is configured to strideacross the fin FA via the gate insulating film GIt. Likewise, in thememory cell portion A3, in the short-side direction of the fin FA, thememory gate electrode MG extends along the main surface FAa and sidesurfaces FAs of the fin FA via the gate insulating film GIm, and alsoextends over the element isolation film STM that encloses the fin FA.That is, the memory gate electrode MG is configured to stride across thefins FA via the gate insulating film GIm.

In the memory cell portions A1 and A4, the source region MS and thedrain region MD are disposed outside the control gate electrode CG andthe memory gate electrode MG to sandwich the control gate electrode CGand the memory gate electrode MG. The source region MS has an n⁻-typesemiconductor region EX1 and the epilayer EP1, while the drain region MDhas an n⁻-type semiconductor region EX2 and the epilayer EP2. Then⁻-type semiconductor regions EX1 and EX2 are n-type semiconductorregions in which n-type impurities are introduced into the fin FA. Theepilayers EP1 and EP2 are silicon epitaxial layers formed on the uppersurface FAa and side surfaces FAs of the fin FA. The epilayers EP1 andEP2 have n-type impurities, such as phosphorus (P), introduced thereintoat a high concentration. The concentration of impurities in each of theepilayers EP1 and EP2 is higher than that in each of the n⁻-typesemiconductor regions EX1 and Ex2.

Over sidewalls of the control gate electrode CG and memory gateelectrode MG, sidewall spacers (sidewalls, or sidewall insulating films)SW and an interlayer insulating film IL1 are formed. Furthermore, aninterlayer insulating film IL2 is formed over the interlayer insulatingfilm IL1 to cover the control gate electrode CG, the memory gateelectrode MG, the source region MS, and the drain region MD. The metalwirings MW are formed on the interlayer insulating film IL2. The metalwirings MW are electrically coupled to the source region MS and thedrain region MD via the plug electrodes PG provided in the contact holesCT formed in the interlayer insulating films IL2 and IL1. Note that asilicide layer SC is formed on the surface of each of the epilayers EP1and EP2, and the plug electrode PG is in contact with the silicide layerSC.

The memory cell MC includes the control gate electrode CG, the memorygate electrode MG, the drain region MD, and the source region MS, whichare formed at the fin FA. The control gate electrode CG is disposed overthe main surface FAa and side surfaces FAs of the fin FA via the gateinsulating film GIt. The memory gate electrode MG is disposed over themain surfaces FAa and side surfaces FAs of the fin FA via the gateinsulating film GIm. The drain region MD and the source region MS aredisposed to sandwich therebetween the control gate electrode CG and thememory gate electrode MG. A distance in the long-side direction betweenthe drain region MD and the source region MS corresponds to a channellength of the memory cell MC. A region where the control gate electrodeCG or memory gate electrode MG in the short-side direction faces themain surface FAa and side surfaces FAs of the fin FA corresponds to achannel width of the memory cell MC.

As shown in FIG. 12, the fins FB as the protrusions of the semiconductorsubstrate 1 are formed in the logic portion B of the semiconductorsubstrate 1. Each fin FB has its lower part enclosed by the elementisolation film STL formed over the main surface 1 a of the semiconductorsubstrate 1. That is, the adjacent fins FB are separated from each otherby the element isolation film STL. A p-type well PW2, which is a p-typesemiconductor region, is formed in a lower part of the fin FB. In otherwords, the fin FB is formed within the p-type well PW2.

In the logic portion B1, the transistor Tr includes a gate electrode GE,and a source region LS and a drain region LD arranged on both ends ofthe gate electrode GE, all of which are formed at the fin FB. The gateelectrode GE is formed over the main surface FBa and side surfaces FBsof the fin FB via the gate insulating film GIL and the insulating filmHK. The gate insulating film GIL is a thermally oxidized film and has athickness of approximately 1 to 2 nm. In the logic portion B2, in theshort-side direction of the fin FB, the gate electrode GE extends alongthe main surface FBa and side surfaces FBs of the fin FB via the gateinsulating film GIL and the insulating film HK, and also extends overthe element isolation film STL that encloses the fin FB. The gateelectrode GE has a laminated structure including the metal films ME1 andME2.

The source region LS and the drain region LD are disposed outside thegate electrode GE to sandwich the gate electrode GE therebetween. Eachof the source region LS and the drain region LD has an n⁻-typesemiconductor region EX3 and the epilayer EP3. The source region LS andthe drain region LD are formed across the entire fin FB exposed from theelement isolation film STL in the short-side direction and in the heightdirection. In the logic portion B3, the source region LS is configuredof the fin FB and the epilayer EP3 formed over the main surface FBa andside surfaces FBs of the fin FB. The epilayer EP3 is a silicon epitaxiallayer formed on the upper surface FBa and side surfaces FBs of the finFB. The epilayer EP3 has n-type impurities, such as phosphorus (P),introduced thereinto at a high concentration. The concentration ofimpurities in the epilayer EP3 is higher than that in the n⁻-typesemiconductor region EX3. The drain region LD also has the samestructure as the source region LS.

Over sidewalls of the gate electrode GE, sidewall spacers SW and theinterlayer insulating film IL1 are formed. Furthermore, the interlayerinsulating film IL2 is formed over the interlayer insulating film IL1and the gate electrode GE. The metal wirings MW are formed on theinterlayer insulating film IL2. The metal wirings MW are electricallycoupled to the source region LS and the drain region LD via the plugelectrodes PG provided in the contact holes CT formed in the interlayerinsulating films IL2 and IL1. Note that the silicide layer SC is formedon the surface of each epilayer EP3, and the plug electrode PG is incontact with the silicide layer SC.

Note that the p-type wells PW1 and PW2 are shown only in FIGS. 11 and12, and will be omitted in cross-sectional views for other manufacturingmethods.

<Manufacturing Steps for Semiconductor Device>

Now, the manufacturing steps for the semiconductor device in thisembodiment will be described. First, the fin formation step will bedescribed, and then the formation methods for the memory cell in thememory cell portion and the MISFET in the logic portion will bedescribed below. The fin formation method in this embodiment is based onthe consideration example described above, and thus only differentpoints from the above-mentioned fin formation step will be mainlydescribed. FIGS. 13 to 28 are cross-sectional views of main parts in theformation steps for the semiconductor device in this embodiment.

Now, a description will be given on the importance of setting the widthof the fin FA in the memory cell portion A wider (larger) than that ofthe fin FB in the logic portion B.

As mentioned above, the insulating film 10′ (of 5 to 6 nm in thickness)as the thermally oxidized film is formed on the main surface FAa andside surface FAs of the fin FA in the part covered with the memory gateelectrode MG. The thickness of the insulating film 10′ is preferablythicker than that of the gate insulating film GIt or the gate insulatingfilm GIL (of 1 to 2 nm in thickness) formed of the thermally oxidizedfilm on the main surface FBa and side surfaces FBs of the fin FB in thelogic portion B. This is because the insulating film 10′ located underthe insulating film 11′, which serves as the charge storage portion, isthickened, thereby making it possible to increase the charge retentiontime and the number of rewritable times of the memory cell MC.

Since the width of the fin FA in the memory cell portion A is decreasedby at least approximately twice as large as the thickness of theinsulating film 10′, the fin FA needs to be thickened by the decrease inadvance. On the other hand, the gate insulating film GIL (of 1 to 2 nmin thickness) formed of the thermally oxidized film on the main surfaceFBa and side surfaces FBs of the fin FB in the logic portion B isthinner than the insulating film 10′. Furthermore, the width of the finFB in the logic portion B needs to be set as narrow as possible,bringing the substrate part of the MISFET formed there into a completedepletion state, thereby reducing the leak current.

In view of the foregoing background, it is important to set the width ofthe fin FA in the memory cell portion A wider (larger) than that of thefin FB in the logic portion B beforehand.

Now, the manufacturing steps of the fin FA in the memory cell portion Aand the fin FB in the logic portion B will be described with referenceto FIGS. 13 to 15.

Like the above-mentioned considered example, the processes from theprovision step (step S1) of the semiconductor substrate to the finformation step (step S6) are performed in sequence. Note that theline-thinning step for the hard mask film 5 b in the hard-mask-filmformation step (step S4) is not performed. That is, as shown in FIG. 13,fins F3 with an equal width are formed in the memory cell portion A andthe logic portion B. The width of each fin F3 is, for example,approximately 30 nm. The fins F3 are exposed from the element isolationfilms STM and STL by approximately 50 nm.

Then, as shown in FIG. 14, a line-thinning step (step S7) of the fins iscarried out. Isotropic etching is applied to the fins F3 made of siliconin the logic portion B by using a photoresist film (mask film) PR2covering the memory cell portion A and exposing the logic portion B as amask. The above-mentioned fins F3 in the logic portion B are selectivelythinned, so that fins F4 are formed in the logic portion B. The fin F4has, for example, a width of approximately 10 to 15 nm and a height ofapproximately 35 to 40 nm. The isotropic etching in use is, for example,dry etching using a mixed gas of CF₄ and O₂. After forming the fins F4,the photoresist film PR2 is removed. Subsequently, parts of the fins F4in the logic portion B and the fins in the memory cell portion A may becovered with a mask (not shown) (made of, for example, a photoresistfilm), and the above-mentioned isotropic etching may be applied to theexposed parts of the fins F4, thereby producing narrower fins.Furthermore, these steps are repeated to enable the formation of two ormore kinds of fins with different widths in the logic portion B.

Then, after removing the photoresist film PR2, as shown in FIG. 15, thesemiconductor substrate 1 having the fins FA in the memory cell portionA and the fins FB in the logic portion B can be provided. In the memoryportion A, the width of a part of each fin FA exposed from the elementisolation film STM is substantially equal to that of a part of the finFA embedded in the element isolation film STM. Here, such a width W3 isapproximately 30 nm. A height H1 of the part of the fin FA exposed fromthe element isolation film STM is approximately 50 nm. In the logicportion B, a width W4 of a part of each fin FB exposed from the elementisolation film STL is approximately 10 to 15 nm, and a width W5 of apart of the fin FB embedded in the element isolation film STL isapproximately 30 nm. A height H2 of the part of the fin FB exposed fromthe element isolation film STL is approximately 35 to 40 nm. That is,the width W5 of the part of the fin FB embedded in the element isolationfilm STL is wider than the width W4 of the part of the fin FB exposedfrom the element isolation film STL, whereby a shoulder portion SH of apart of the fin FB embedded in the element isolation film STL is exposedfrom the element isolation film STL.

In this way, the isotropic etching is applied to the fins made ofsilicon to make the width of each fin narrower, which can reducevariations in the etching amount and in the fin width across the planeof the semiconductor wafer, thereby producing a stable fin formationmethod. The processing accuracy of the fins can be improved to achievethe miniaturization and highly integrated configuration of the logicportion B. The dry etching of silicon has a lower etching rate than wetetching of a silicon oxide film, resulting in better controllability ofthe etching amount. The controllability of etching is high because ofthe dry etching, thereby making it possible to reduce variations in theetched state across the plane.

Next, the manufacture of the memory cell MC and the transistor Tr willbe described with reference to FIGS. 16 to 28. FIGS. 16 to 25, FIG. 27,and FIG. 28 illustrate cross-sectional views of the memory cell portionsA1, A2, and A3 shown in FIG. 11 and cross-sectional view of the logicportions B1 and B2 shown in FIG. 12. FIG. 26 shows the cross-sectionalviews of the memory cell portion A4 and the logic portion B3.

FIG. 16 illustrates the cross-sectional view of the memory cell portionsA1, A2, and A3 and the logic portions B1 and B2, with the fins FA and FBshown in FIG. 15.

FIG. 17 shows a formation step (step S8) of an insulating film 7, aconductive film 8, and an insulating film 9. First, the insulating film7 is formed over the main surfaces FAa and FBa and side surfaces FAs andFBs of the fins FA and FB. The insulating film 7 is formed by thermallyoxidizing the main surfaces FAa and FBa and side surfaces FAs and FBs ofthe fins FA and FB, thereby forming silicon oxide films of approximately2 nm in thickness. Then, the conductive film 8 is deposited over theinsulating film 7 to be positioned at a level higher than the height ofeach of the fins FA and FB, followed by a CMP process on the conductivefilm 8, thereby producing the conductive film 8 with a flat mainsurface. Then, the insulating film 9 is deposited over the main surfaceof the conductive film 8. The conductive film 8 is made of a polysiliconfilm (silicon film), while the insulating film 9 is made of a siliconnitride film. In the CMP step of the conductive film 8, it is importantto leave the conductive film 8 over the main surfaces of the fins FA andFB. As will be described later, the insulating film 9 preferably has athickness that is substantially the same as the height of the fin FA,but it is noted that FIG. 17 and other drawings show the insulating film9 in a thinned state.

FIG. 18 shows a formation step (step S9) of the control gate electrodeCG. A photoresist film (mask film) PR3 is selectively formed over theinsulating film 9. The photoresist film PR3 has a pattern that coversformation regions for the control gate electrodes CG and exposes otherregions in the memory cell portion A. Furthermore, the photoresist filmPR3 has a pattern covering the logic portion B. A dry etching process isapplied to the insulating film 9 and the conductive film 8 to remove theregions of the insulating film 9 and conductive film 8 exposed from thephotoresist film PR3, thereby forming the control gate electrodes CG.The insulating film 7 is processed by the dry etching process or thefollowing cleaning process, whereby the gate insulating film GIt isformed under the control gate electrodes CG. In the memory cell portionA3, the insulating film 9, the conductive film 8, and the insulatingfilm 7 are removed to expose the main surface FAa and side surfaces FAsof each fin FA. The photoresist film PR3 is removed after patterning theinsulating film 9 or after patterning the insulating film 9 and theconductive film 8.

FIG. 19 shows a formation step (step S10) of insulating films 10 and 11and a conductive film 12. First, insulating films 10 and 11 are formedsequentially over the main surface FAa and side surfaces FAs of each finFA exposed from the control gate electrode CG. The insulating film 10 isa silicon oxide film formed by thermally oxidizing the main surface FAaand side surfaces FAs of the fin FA. The insulating film 10 has athickness of 5 to 6 nm, which is larger than that of the gate insulatingfilm GIt. Then, the insulating film 11 has a laminated film thatincludes a silicon nitride film and a silicon oxynitride film formedover the silicon nitride film. The thickness of the silicon nitride filmis 7 nm, and the thickness of the silicon oxynitride film is 9 nm. Notethat the insulating film 11 may be a laminated film of a lower layer ofHfSiO and an upper layer of AlO.

Then, a conductive film 12 is deposited over the insulating film 11. Theconductive film 12 has such a thickness that is larger than each of theheight of the laminated body of the control gate electrode CG andinsulating film 9, and the height of the fin FA in the memory cellportion A3. The CMP process is applied to the conductive film 12 toexpose the insulting film 11 located over the control gate electrode CG,whereby as shown in FIG. 19, the conductive film 12 is selectivelyformed in the regions exposed from the control gate electrodes CG in thememory cell portion A. After the CMP process, the conductive film 12 isleft over the fin FA in the memory cell portion A3. Note that theconductive film 12 is made of a polysilicon film (silicon film). In thelogic portion B, the conductive film 12 is removed to expose theinsulating film 11.

FIG. 20 shows an etch-back step (step S11) of the conductive film 12. Anetching process is applied to the conductive film 12 in the memory cellportion A to thereby lower the height of the main surface of theconductive film 12. After the etch-back process, the main surface of theconductive film 12 has substantially the same height as, for example,the main surface of the control gate electrode CG.

FIG. 21 shows a formation step (step S12) of the control gate electrodeCG. A silicon nitride film is deposited over the sidewalls of theinsulating films 9 and 11 over the control gate electrode CG and overthe conductive film 12, followed by anisotropic etching, thereby forminga mask film 13 over the sidewalls of the insulating films 9 and 11 onthe control gate electrode CG. A part of the conductive film 12 exposedfrom the mask film 13 is removed by etching, whereby the memory gateelectrode MG and a spacer SP are formed over the respective sidewalls ofthe control gate electrode CG via the insulating films 10 and 11. Notethat although the spacer SP has the substantially same structure as thememory gate electrode MG, it is removed in a subsequent step. This iswhy the spacer is denoted by a different name.

FIG. 22 shows a step of removal of the spacer SP and formation of a gateinsulating film GIm (step S13). First, the spacer SP and the mask film13 over the spacer SP shown in FIG. 21 are removed, for example, by awet etching process using a resist film (not shown) covering the memorygate electrode MG and exposing the spacer SP. Subsequently, parts of theinsulating films 11 and 10 in the regions exposed from the memory gateelectrode MG are removed, for example, by the wet etching process, sothat insulating films 11′ and 10′ are selectively left under the memorygate electrode MG (i.e., between the memory gate electrode MG and thefin FA), and the gate insulating film GIm is formed. Note that the gateinsulating films GIm are continuously formed not only between the mainsurface FAa of the fin FA and the memory gate electrode MG, but alsobetween the control gate electrode CG and the memory gate electrode MG.The gate insulating film GIm shown in FIG. 22 is formed along the mainsurface FAa and side surfaces FAs of the fin FA.

FIG. 23 shows a formation step (step S14) of a dummy gate DG and then⁻-type semiconductor regions (impurity diffusion layers) EX1, EX2, andEX3. First, in the logic portion B, the insulating film 9 and theconductive film 8 are patterned to form the dummy gate DG. Theinsulating film 9 over the dummy gate DG and the insulting film 7 underthe dummy gate DG have the same planar pattern as the dummy gate DGitself does.

Then, n-type impurities, such as arsenic (As) or phosphorus (P), areintroduced into the fins FA and FB by ion implantation, so that n⁻-typesemiconductor regions EX1 and EX2 are formed in the fin FA, and n⁻-typesemiconductor regions EX3 are formed in the fin FB. The n⁻-typesemiconductor regions EX1 and EX2 are formed in self-alignment with thecontrol gate electrode CG and the memory gate electrode MG. That is, then-type impurities are implanted into the main surface and side surfacesof the fin FA exposed from the control gate electrode CG and the memorygate electrode MG, whereby the n⁻-type semiconductor regions EX1 and EX2are formed on both sides of the control gate electrode CG and the memorygate electrode MG to sandwich therebetween the control gate electrode CGand the memory gate electrode MG. Since impurities are diffused by aheat treatment after the ion implantation, the n⁻-type semiconductorregion EX1 partially overlaps with the memory gate electrode MG, whilethe n⁻-type semiconductor region EX2 partially overlaps with the controlgate electrode CG.

The n⁻-type semiconductor regions EX3 are formed in self-alignment withthe dummy gate DG. That is, n-type impurities are implanted into themain surface and side surfaces of the fin FB exposed from the dummy gateDG, whereby the n⁻-type semiconductor regions EX3 are formed at bothsides of the dummy gate DG to sandwich the dummy gate DG therebetween.Since impurities are diffused by a heat treatment after the ionimplantation, the n⁻-type semiconductor region EX3 partially overlapswith the dummy gate DG.

FIG. 24 shows a formation step (step S15) of a sidewall spacer(sidewall, sidewall insulating film) SW. An insulating film, forexample, of a silicon oxide film or silicon nitride film or a laminatedfilm thereof, is deposited over the semiconductor substrate 1 to coverthe main surfaces FAa and FBa of the fins FA and FB, followed by theanisotropic etching on the insulating film. In this way, in the memorycell portion A1, the sidewall spacers SW are formed not only over thesidewall of the control gate electrode CG and the insulating film 9, butalso the sidewall of the memory gate electrode MG and the mask film 13.Here, the thickness of the insulating film 9 is substantially the sameas the height of the fin FA, thereby enabling sufficient overetching.Thus, for example, the silicon oxide film or silicon nitride film forformation of the sidewall spacer SW never remains over the elementisolation film STM enclosing the fin FA.

In the logic portion B1, the sidewall spacers SW are formed over thesidewalls of the dummy gate DG and the insulating film 9. By theabove-mentioned anisotropic etching, the insulating films for formationof the sidewall spacer SW are removed from the memory cell portions A2and A3 and the logic portion B2 to expose the insulating film 9 or maskfilm 13.

Next, FIGS. 25 and 26 show a formation step (step S16) of the epilayersEP1, EP2, and EP3 and the silicide layer SC. In the memory cell portionA, the epilayers EP1 and EP2 are formed at the main surface FAa and sidesurfaces FAs of the fin FA exposed from the element isolation film STM,control gate electrode CG, memory gate electrode MG, and sidewallspacers SW. The epilayer EP3 is also formed in the same step at the mainsurface FBa and side surfaces FBs of the fin FB exposed from the elementisolation film STL, dummy gate DG, and sidewall spacers SW. Theepilayers EP1, EP2, and EP3 are formed by epitaxially growing SiH₂Cl₂(SiH₄) using HCl, and PH₃ gas under an atmosphere at 100 Pa and 700° C.That is, the epilayers EP1, EP2, and EP3 are semiconductor layers dopedwith n-type impurities in a higher concentration than those in then⁻-type semiconductor regions EX1, EX2, or EX3. As shown in the logicportion B3 shown in FIG. 26, the shoulder portion SH of the part of thefin FB embedded in the element isolation film STL is exposed from theelement isolation film STL in the logic portion B. Thus, epitaxialgrowth can also proceed out of the shoulder portion SH of the fin FB,thereby increasing the deposition amount of the epilayer EP3, comparedto the case in which no shoulder portion SH is provided, thus decreasinga parasitic resistance of the source region LS and the drain region LD.

Note that when forming a p-type MISFET in the logic portion B, a p-typeSiGe epilayer can be formed at the main surface FBa and side surfacesFBs of the fin FB exposed from the element isolation film STL, dummygate DG, and sidewall spacers SW. The p-type SiGe epilayer is formed byepitaxially growing SiH₂Cl₂ (SiH₄) using GeH₄, HCl, and B₂H₆ gas underan atmosphere at 100 Pa and 700° C. The formation of the SiGe epilayercan reduce the parasitic resistances in the source region and drainregion of the p-type MISFET, while improving the hall mobility byapplying stress to the channel region, enabling a high-speed operationof the p-type MISFET.

Furthermore, as shown in FIGS. 25 and 26, a silicide layer SC is formedat the surfaces of the epilayers EP1, EP2, and EP3. The silicide layerSC can be preferably a cobalt silicide layer, a nickel silicide layer,or a platinum-added nickel silicide layer.

In this way, the source region MS of the memory cell MC is configured ofthe n⁻-type semiconductor region EX1 and the epilayer EP1 containing ahigher concentration of n-type impurities than the n⁻-type semiconductorregion EX1, while the drain region MD of the memory cell MC isconfigured of the n⁻-type semiconductor region EX2 and the epilayer EP2containing a higher concentration of n-type impurities than the n⁻-typesemiconductor region EX2. Furthermore, each of the source region LS anddrain region LD of the transistor Tr in the logic portion B isconfigured of the n⁻-type semiconductor region EX3 and the epilayer EP3containing a higher concentration of n-type impurities than the n⁻-typesemiconductor region EX3.

FIG. 27 shows a formation step (step S17) of an interlayer insulatingfilm IL1. The interlayer insulating film IL1 is formed (deposited) overthe semiconductor substrate 1. The interlayer insulating film IL1 is asingle film made of a silicon oxide film, or a laminated film includinga silicon nitride film and a silicon oxide film formed on the siliconnitride film more thickly than the silicon nitride film. The interlayerinsulating film IL1 can be formed, for example, using a CVD method.Then, polishing (polishing process) is performed on the upper surface ofthe interlayer insulating film IL1 by the CMP method and the like. Asshown in FIG. 27, the respective upper surfaces of the control gateelectrode CG, the memory gate electrode MG, and the dummy gate electrodeDG are exposed. That is, in the polishing step, parts of the insulatingfilm 9 and the mask film 13 formed over the control gate electrode CG,the memory gate electrode MG, and the dummy gate electrode DG arecompletely removed. Obviously, the sidewalls SW positioned over thesidewalls of the insulating film 9 and the mask film 13 are also partlyremoved.

FIG. 28 shows a formation step (step S18) of the gate electrode GE.First, a removal step of the dummy gate DG exposed as shown in FIG. 27is performed. The removal of the dummy gate DG forms a groove in theinterlayer insulating film IL1. The bottom part (bottom surface) of thegroove is formed by the upper surface of the insulating film 7, and thesidewall (side surface) of the groove is formed by the side surface ofthe sidewall spacer SW (side surface in contact with the dummy gate DGbefore removal of the dummy gate DG). Then, as shown in FIG. 28, aformation step of an insulating film HK, a metal film ME1, and a metalfilm ME2 is carried out to sequentially deposit the insulating film HK,the metal film ME1, and the metal film ME2 over the semiconductorsubstrate 1, i.e., over the insulating film 7 inside (the bottom portionand sidewalls) of the groove. Further, a CMP process step is applied tothe insulating film HK, the metal film ME1, and the metal film ME2. Inthis way, a laminated structure is selectively formed within the groove.The laminated structure includes the gate insulating film GIL made ofthe insulating film 7, the insulating film HK, the metal film ME1, andthe metal film ME2, which are stacked on each other. Here, theinsulating film HK is an insulating material film having a higherdielectric constant (relative permittivity) than that of siliconnitride, i.e., the so-called High-k film (high-dielectric-constantfilm).

The insulating film HK in use can be a metal oxide film, including ahafnium oxide film, a zirconium oxide film, an aluminum oxide film, atantalum oxide film, or a lanthanum oxide film. The insulating film HKcan be formed, for example, by an Atomic Layer Deposition (ALD) methodor the CVD method.

For example, the metal film ME1 can be a titanium aluminum (TiAl) film,and the metal film ME2 can be an aluminum (A1) film. A titanium (Ti)film, a titanium nitride (TiN) film, or a laminated film thereof may beinterposed between the metal films ME1 and ME2 to adjust a thresholdvoltage of the transistor Tr.

The insulating film HK is formed over the bottom part (bottom surface)and sidewalls of the groove, while the gate electrode GE has its bottompart (bottom surface) and sidewalls (side surfaces) adjacent to theinsulating film HK. The insulating film GIL and the insulating film HKare interposed between the gate electrode GE and the fin FB of thesemiconductor substrate 1. The insulating film HK is interposed betweenthe gate electrode GE and the sidewall spacer SW. The gate insulatingfilm GIL and the insulating film HK directly under the gate electrode GEserve as the gate insulating film of the transistor Tr. The insulatingfilm HK is a high dielectric constant film and thus serves as ahigh-dielectric-constant gate insulating film.

Then, a formation step (step S19) of the interlayer insulating film IL2,the plug electrode PG, and the metal wiring MW will be described withreference to FIGS. 11 and 12. The interlayer insulating film IL2 isformed over the interlayer insulating film IL. The interlayer insulatingfilm IL2 in use can be, for example, a silicon oxide-based insulatingfilm mainly consisting of silicon oxide. After forming the interlayerinsulating film IL2, the upper surface of the interlayer insulating filmIL2 is polished by the CMP method to enhance the flatness of the uppersurface of the interlayer insulating film IL2.

Then, contact holes (openings, through holes) CT are formed in theinterlayer insulating films IL1 and IL2. The contact holes CT expose thesurfaces of the silicide layers SC in the source region MS and drainregion MD in the memory cell MC, and expose the surfaces of the silicidelayers SC in the source region LS and drain region LD in the transistorTr.

Then, a conductive plug PG made of, e.g., tungsten (W), is formed as aconductor for coupling in each contact hole CT. The plug electrode PGhas a laminated structure including a barrier conductive film (e.g., atitanium film, a titanium nitride film, or a laminated film thereof),and a main conductive film (tungsten film) positioned on the barrierconductive film. The plug electrodes PG are electrically coupled withthe source region MS and drain region MD in the memory cell MC, and withthe source region LS and drain region LD in the transistor Tr.

Then, a metal wiring MW is formed over the interlayer insulating filmIL2. The metal wiring MW has a laminated structure including a barrierconductive film (e.g., a titanium nitride film, a tantalum film, or atantalum nitride film) and a main conductive film (copper film) formedon the barrier conductive film. For simplifying the drawing, FIGS. 11and 12 illustrate the state in which the barrier conductive film and themain conductive film are integrated together to form the metal wiringMW. The same goes for the plug electrode PG.

The epilayers EP are formed in the source region MS and drain region MDin the memory cell MC as well as in the source region LS and drainregion LD in the transistor Tr, which can prevent misalignment of themask when forming the contact hole CT, while reducing a contactresistance between the plug electrode and the epilayer EP.

<Main Features and Effects>

Next, the main features and effects of this embodiment will bedescribed.

In the manufacturing method for the semiconductor device in thisembodiment, when forming the active regions with two or more kinds offin widths, the fins with an equal width are formed in the respectivefirst and second regions of the semiconductor substrate, and then, forexample, the fins formed of silicon in the second region are selectivelyetched to fabricate another size of fins that have a narrower width inthe second region than that of the fins in the first region. In thisway, the dry etching process is applied to the fins made of silicon, sothat the fins can be produced with higher processing accuracy, comparedto the case of performing a line-thinning process by wet etching of ahard mask made of an insulating film for processing fins. Sincevariations in the processing can be reduced, the manufacturing yield canbe improved.

The use of the isotropic etching for the above-mentioned etching processcan also exhibit the effect of reducing any defect on the main surfaceor side surfaces of the fins with the narrower width formed in thesecond region. The use of the anisotropic dry etching would have theproblem of causing etching damages (e.g., defects) on the side surfaceof the fins, or of attaching an etching product (polymer) onto the sidesurface of the fins when forming the fins with the equal width in thefirst and second regions. However, the etching damages and etchingproducts can be removed by the isotropic etching with no damage.

The fin has its periphery covered with the element isolation film, andthe part of the fin protruding from the element isolation film issubjected to the etching. To decrease the fin width, the fin isconfigured to have a first part with a wide width which has itsperiphery covered with the element isolation film, and a second partwith a narrow width which is exposed from the element isolation film.The shoulder portion exposed from the upper surface of the elementisolation film exists at the boundary between the first part and thesecond part. When the epitaxial growth proceeds on the main surface andside surfaces of the fin, the epitaxial growth also proceeds at theshoulder portion, so that the deposition of the epilayer formed aroundthe fin can be promoted. Thus, the parasitic resistance of the sourceregion and drain region in the MISFET with the epilayer formed thereatcan be reduced.

The structure with the shoulder portion can reduce the leak current fromthe MISFET formed in the fin with the narrow width, while reducing theparasitic resistances in the source region and drain region of theMISFET. This is because the fin with the narrower width can becompletely brought into the depletion state.

Modified Example

A modified example is proposed to achieve the second improvement, anddiffers from the above-mentioned considered example in a hard-mask-filmformation step (step S4). FIGS. 29 to 31 are cross-sectional views ofmain parts in the manufacturing steps for the semiconductor device inthe modified example.

Like the above-mentioned considered example, the processes from theprovision step (step S1) of the semiconductor substrate up to themask-film formation step (step S3) will be performed in turn. Then, aninsulating film made of a silicon oxide film is deposited over the mainsurface of the semiconductor substrate 1 to cover the upper surface andside surfaces of each of the mask films 4 a and 4 b, like the consideredexample. Then, as shown in FIG. 29, anisotropic etching is applied tothe insulating film to form sidewall insulating films 29 a and 29 b overthe sidewalls of the mask film 4 a and 4 b. Each sidewall insulatingfilm 29 a is formed in the memory cell portion A, while each sidewallinsulating film 29 b is formed in the logic portion B. Both sidewallinsulating films 29 a and 29 b have an equal width.

Subsequently, as shown in FIG. 30, the sidewall insulating films 29 b inthe logic portion B are removed by using a photoresist film (mask film)PR4 that covers the memory cell portion A and exposes the logic portionB.

Then, as shown in FIG. 31, an insulating film made of a silicon oxidefilm is deposited over the main surface of the semiconductor substrate 1to cover the mask films 4 a and 4 b and sidewall insulating films 29 a.The insulating film is subjected to anisotropic etching to thereby formsidewall insulating films 31 a over the sidewalls of the mask films 4 avia the sidewall insulating films 29 a, as well as sidewall insulatingfilms 31 b over the sidewalls of the mask films 4 b. That is, thesidewall insulating films 29 a and 31 a formed over the sidewalls of themask film 4 a correspond to the hard mask film 5 a in the consideredexample. The sidewall insulating films 31 b formed on the sidewalls ofthe mask film 4 b correspond to hard mask films 5 b′ subjected toline-thinning in the considered example. After forming the sidewallinsulating films 29 a, 31 a, and 31 b, steps S5 and S6 in the consideredexample and further steps to be performed after the step S8 in thisembodiment are carried out, thereby completing the semiconductor devicein the modified example.

In this way, the hard mask film 5 a in the memory cell portion A is madeof a laminated structure of the sidewall insulating films 29 a and 31 a,whereby the thickness of the insulating film for forming the sidewallinsulating film 29 a can be smaller than that of the insulating film 5in the considered example. Thus, the MISFETs formed in the logic portionB can be miniaturized without filling an interval between the adjacentmask films 4 b in the logic portion B.

Although the invention made by the inventors have been specificallydescribed based on the embodiments, it is apparent that the invention isnot limited to the embodiments, and that various modifications andchanges can be made to those embodiments without departing from thescope of the invention.

What is claimed is:
 1. A method for manufacturing a semiconductordevice, comprising the steps of: (a) providing a semiconductor substratewith a main surface; (b) forming a first mask film in each of a firstregion and a second region of the main surface of the semiconductorsubstrate; (c) forming a second mask film over sidewalls of the firstmask film in each of the first region and the second region; (d)removing the second mask film in the second region while leaving thesecond mask film in the first region; (e) forming a third mask film notonly over sidewalls of the first mask film via the second mask film inthe first region, but also directly on sidewalls of the first mask filmin the second region; (f) after removing the first mask film, forming afirst convex portion under the second mask film and the third mask filmby providing first concave portions in the first region through etchingof parts of the semiconductor substrate located outside the second maskfilm and the third mask film, the first convex portion having a firstwidth, while forming a second convex portion under the third mask filmby providing second concave portions in the second region throughetching of parts of the semiconductor substrate located outside thethird mask film, the second convex portion having a second width; (g)forming a first gate electrode to stride across the first convex portionvia a first insulating film in the first region; and (h) forming asecond gate electrode to stride across the second convex portion via asecond insulating film in the second region, wherein the second width isnarrower than the first width.
 2. The method for manufacturing asemiconductor device according to claim 1, wherein the first insulatingfilm is formed by thermally oxidizing the first convex portion, whereinthe second insulating film is formed by thermally oxidizing the secondconvex portion, and wherein a thickness of the first insulating film islarger than that of the second insulating film.
 3. The method formanufacturing a semiconductor device according to claim 1, furthercomprising the step of: (i) between the step (f) and the step (g),forming an element isolation film made of an insulating film to cover aperiphery of each of the first convex portion and the second convexportion at respective lower parts of the first convex portion and thesecond convex portion.
 4. The method for manufacturing a semiconductordevice according to claim 3, wherein in the step (g), the firstinsulating film includes a silicon oxide film formed at a surface of thefirst convex portion and a silicon nitride film formed over the siliconoxide film.
 5. The method for manufacturing a semiconductor deviceaccording to claim 1, wherein in the step (f), anisotropic etching isused as the etching of the semiconductor substrate.